RECOMMENDED FOR
Small Structures
PRODUCTION


Description
SCIGRIP® SG200 Series Methacrylate Adhesives are two-component, 10:1 mix ratio products for bonding composites, thermoplastics, metals and combinations thereof. Minimal surface preparation combined with a choice of 10, 20, and 40 minute working times, provide reduced labor and production cycle time. These products are widely used for marine, transportation and general plastic bonding applications.
Features & Benefits
- Choice of 10, 20, and 40 minute working times
- Outstanding sag resistance for application on non-level surfaces
- Excellent environmental and chemical resistance
- Minimal surface preparation, however metals require primer
RECOMMENDATIONS & SURFACE PREP | |||
---|---|---|---|
![]() Best | ![]() Test | ![]() Primer | ![]() Prep |
METALS | |
---|---|
Aluminum | ![]() |
Coated/Painted Metals | ![]() |
Plated Metals | ![]() |
Sheet Metal | ![]() |
Stainless Steel | ![]() |
Cold Rolled Steel | ![]() |
THERMOPLASTICS | |
---|---|
ABS | ![]() |
Acrylics | ![]() |
Vinyls (PVC) | ![]() |
THERMOSET COMPOSITES | |
---|---|
Fiberglass | ![]() |
Gelcoats | ![]() |
RTM & RTM Light | ![]() |
What Are You Bonding Together?
SPECIFICATIONS & AVAILABILITY
Working Times
Adhesive | Gap Fill Inch (mm) | Working Time min. | Fixture Time |
---|---|---|---|
SG200-10 | 0.02-0.5 (0.50-12.7) | 8-12 | 25-30 |
SG200-20 | 0.02-0.5 (0.50-12.7) | 17-22 | 35-42 |
SG200-40 | 0.02-0.5 (0.50-12.7) | 35-45 | 80-90 |
Typical Physical Properties
Adhesive | Ratio A:B Volume Weight | ||
---|---|---|---|
SG200-10 | 10:1 | ||
SG200-20 | 10:1 | ||
SG200-40 | 10:1 |
Typical Cured Properties
Adhesive | Tensile Strength psi (MPa) %Elongation | Shear Strength psi (MPa) |
---|---|---|
SG200-10 | 3,000-3,500 (17-21) 60-100 | 2,200-2,500 (15-17) |
SG200-20 | 3,000-3,500 (17-21) 60-100 | 2,200-2,500 (15-17) |
SG200-40 | 3,000-3,500 (17-21) 60-100 | 2,200-2,500 (15-17) |
Availability & Handling

Product Certifications
![]() | |
---|---|
This SCIGRIP product is GREENGUARD certified for low chemical emissions |